TP347 TP347H 1.4550 1.4961 Stainless Steel Pipe and Tube

Alloy 347 (UNS S34700) is columbium stabilized austenitic stainless steel plate with good general corrosion resistance and somewhat better resistance in strong oxidizing conditions than 321 (UNS S32100). It has excellent resistance to intergranular corrosion after exposure to temperatures in the chromium carbide precipitation range of 800 – 1500°F (427 – 816°C). The alloy has good oxidation resistance and creep strength to 1500°F (816°C). It also possesses good low temperature toughness.

Alloy 347H (UNS S34709) stainless steel is the higher carbon (0.04 – 0.10) version of the alloy. It was developed for enhanced creep resistance and for higher strength at temperatures above 1000°F (537°C). In most instances, the carbon content of the plate enables dual certification.

Stainless Seamless Fluid Pipe Quality Control

1. Raw materials pipe blank quality classification: high quality, medium, economical
2. Raw materials inspection after receive in factory
3. After pickled, tube will be grinded careful to less defect
4. Multiple cold drawn/rolled process for precision dimension
5. Standard heat-treated of continuous annealed/solution for better property, intergranular corrosion
6. Full Inspection: ET, UT, Hydraulic Test, Penetration Test, Grinded, Sand Blast, Print Making

*Besides bleow, we can supply comfortable price with equivalents quality for you! Welcome contact us.

We also can supply other kinds of:

• Seamless Stainless Steel Pipe & Tube
• Welded Stainless Steel Pipe & Tube
• U Type Stainless Steel Pipe & Tube
• Coil Type Stainless Steel Pipe & Tube(Max 300meter), seamless or welded
• Annealed Pickled AP Stainless Steel Pipe & Tube (Ra ≤5μm)
• Bright Annealed BA Stainless Steel Pipe & Tube (Ra ≤8μm)
• Mechanical Polished MP Stainless Steel Pipe & Tube (Ra ≤8μm)
• Electro Polished EP Stainless Steel Pipe & Tube (Ra ≤25μm)
• Sanitary Stainless Steel Pipe & Tube
• Capilllary Stainless Steel Pipe & Tube
• Instrument Stainless Steel Pipe & Tube

Applications

Chemical Processing

Food Processing – equipment and storage

Petroleum Refining – fluid catalytic cracking units, polythionic acid service

Pharmaceutical Production

Waste Heat Recovery – recuperators

Equivalent grades of   steel   X6CrNiNb18-10 (1.4550)

DIN	EU EN	USA –	UNS	France AFNOR	England BS	Sweden SS	Russia GOST
1.4550	X6CrNiNb18-10	347	S34700	Z6CNNb18-10	347S31	2338	08KH18N12B
1.4961	X8CrNiNb16-13	347H	S34709

Chemical Properties:

	C	Cr	Mn	Ni	P	S	Si	Cb/Ta
347	0.08 max	min: 17.0 max: 20.0	2.0 max	min: 9.0 max: 13.0	0.04 max	0.30 max	0.75 max	min:10x C max: 1.0
347H	min: 0.04 max: 0.10	min: 17.0 max: 20.0	2.0 max	min: 9.0 max: 13.0	0.03 max	0.30 max	0.75 max	min:10x C max: 1.0

Mechanical Properties:

Grade	Tensile Strength ksi (MPa) min	Yield Strength 0.2% ksi offset ksi (MPa) min	Elongation (% in 50mm) min	Hardness (Brinell) MAX	Hardness (Rockwell B) MAX
347/347H	75 (515)	30 (205)	40	201	95

Stainless Steel Tube & Pipe Sizes:

Outsider Diameter OD : 6-630mm ; WT 3-60mm ; L max 16meter

Stainless Steel Tube Delivery Condition:

• Solution Treatment

Stainless Tube Surface:

Acid pickling – pre-passivation process of treating stainless steel parts with an acid solution, typically hydrochloric or sulfuric acid, which can remove oxide scale and heat tint while dissolving steel flecks embedded in the part.

Polishing – P grade sandpaper: P150, P200, P250, P300, P400, P500, P600, P700, P800

Stainless Pipe Inspection and Testing:

Chamical analysis / Tensile test at room temperature / flattening test / ring tensile test / drift expemdomg test / ring expanding test / leak tightness test / Tensile test at elevated temperature / impact test at room temperature / impact test at low temperature / eddy current test / ultrasonic test / magnetic flux leakage test

Stainless Tube Marking and Packages:

In addition to the marking prescribed in specification as client’s request.

Bare / Nylon / Plastic / Wooden Case

Corrosion Resistance

Alloy 347 stainless steel plate exhibits good general corrosion resistance that is comparable to 304. It was developed for use in the chromium carbide precipitation range of 800 – 1500°F (427 – 816°C) where un-stabilized alloys such as 304 are subject to intergranular attack. In this temperature range, the overall corrosion resistance of Alloy 347 stainless steel plate is superior to Alloy 321 stainless steel plate. Alloy 347 also performs somewhat better than Alloy 321 in strongly oxidizing environments up to 1500°F (816°C).

The alloy can be used in nitric solutions, most diluted organic acids at moderate temperatures and in pure phosphoric acid at lower temperatures and up to 10% diluted solutions at elevated temperatures. Alloy 347 stainless steel plate resists polythionic acid stress corrosion cracking in hydrocarbon service. It can also be utilized in chloride or fluoride free caustic solutions at moderate temperatures.

WELDABILITY

Austenitic stainless steels are considered to be the most weldable out of all high alloy steels

Can be welded by all fusion and resistance welding processes

HEAT TREATMENT

Annealing temperature range is 1800 to 2000°F

May be stress relief annealed within the carbide precipitation range of 800 to 1500°F without any danger of subsequent intergranualr corrosion

Cannot be hardened by heat treatment