317 317L 1.4449 1.4438 Stainless Steel Pipe and Tube

317 is an austenitic chromium-nickel stainless steel that possesses excellent corrosion resistance. Of all the 300 series stainless steels, alloy 317 is the most corrosion resistant and has the highest tensile and creep strength properties at elevated temperatures. The high molybdenum content the alloy’s superior pitting resistance.

317L is a molybdenum containing, low carbon austenitic stainless steel with increased additions of chromium, nickel, and molybdenum for better corrosion resistance and increased resistance to chemical attack for sulfurous, acetic, formic, citric, and tartaric acids. Due to its low carbon content, 317L also provides resistance to sensitization when welded and higher creep, stress to rupture, and tensile strength at elevated temperatures. It is non-magnetic in the annealed condition but may become slightly magnetic after welding.

Stainless Seamless Fluid Pipe Quality Control

1. Raw materials pipe blank quality classification: high quality, medium, economical
2. Raw materials inspection after receive in factory
3. After pickled, tube will be grinded careful to less defect
4. Multiple cold drawn/rolled process for precision dimension
5. Standard heat-treated of continuous annealed/solution for better property, intergranular corrosion
6. Full Inspection: ET, UT, Hydraulic Test, Penetration Test, Grinded, Sand Blast, Print Making

*Besides bleow, we can supply comfortable price with equivalents quality for you! Welcome contact us.

We also can supply other kinds of:

• Seamless Stainless Steel Pipe & Tube
• Welded Stainless Steel Pipe & Tube
• U Type Stainless Steel Pipe & Tube
• Coil Type Stainless Steel Pipe & Tube(Max 300meter), seamless or welded
• Annealed Pickled AP Stainless Steel Pipe & Tube (Ra ≤5μm)
• Bright Annealed BA Stainless Steel Pipe & Tube (Ra ≤8μm)
• Mechanical Polished MP Stainless Steel Pipe & Tube (Ra ≤8μm)
• Electro Polished EP Stainless Steel Pipe & Tube (Ra ≤25μm)
• Sanitary Stainless Steel Pipe & Tube
• Capilllary Stainless Steel Pipe & Tube
• Instrument Stainless Steel Pipe & Tube

APPLICATIONS

317/317L is commonly used to handle sulfur, pulp liquor, acid dyestuffs, acetylating and nitrating mixtures, bleaching solutions, severe coal and oil, and many chemical compounds. Some other applications that use alloy 317L include:

• Paper and pulp handling equipment
• Chemical and petrochemical processing equipment
• Condensers in fossil and nuclear fueled power generation stations
• Food processing equipment
• Textile equipment

Equivalent

ASTM	UNS	EN	DIN	JIS
317	S31700	1.4449	X3CrNiMo18-12-3	SUS317
317L	S31703	1.4438	X2CrNiMo18-15-4	SUS317L

Chemical Properties:

%	Cr	Ni	C	Si	Mn	P	S	Mo	Fe
317	min: 18.0 max:20.0	min: 11.0 max: 15.0	0.080 max	0.75 max	2.0 max	0.04 max	0.03 max	min: 3 max: 4	balance
317L	min: 18.0 max:20.0	min: 11.0 max: 15.0	0.035 max	0.75 max	2.0 max	0.04 max	0.03 max	min: 3 max: 4	balance

Mechanical Properties:

Grade	Tensile Strength ksi (min.)	Yield Strength 0.2% Offset ksi (min.)	Elongation – % in 50 mm (min.)	Hardness (Brinell) MAX	Hardness (Rockwell B) MAX
317	75	30	35	217	95
317L	75	30	40	217	95

Stainless Steel Tube & Pipe Sizes:

Outsider Diameter OD : 6-630mm ; WT 3-60mm ; L max 16meter

Stainless Steel Tube Delivery Condition:

• Solution Treatment

Stainless Tube Surface:

Acid pickling – pre-passivation process of treating stainless steel parts with an acid solution, typically hydrochloric or sulfuric acid, which can remove oxide scale and heat tint while dissolving steel flecks embedded in the part.

Polishing – P grade sandpaper: P150, P200, P250, P300, P400, P500, P600, P700, P800

Stainless Pipe Inspection and Testing:

Chamical analysis / Tensile test at room temperature / flattening test / ring tensile test / drift expemdomg test / ring expanding test / leak tightness test / Tensile test at elevated temperature / impact test at room temperature / impact test at low temperature / eddy current test / ultrasonic test / magnetic flux leakage test

Stainless Tube Marking and Packages:

In addition to the marking prescribed in specification as client’s request.

Bare / Nylon / Plastic / Wooden Case

Corrosion Resistance

The higher molybdenum content of Alloy 317L assures superior general and localized corrosion resistance in most media when compared with 304/304L and 316/316L stainless steels. Environments that don’t attack 304/304L stainless steel will normally not corrode 317L. One exception, however, are strongly oxidizing acids such as nitric acid. Alloys that contain molybdenum generally do not perform as well in these environments.

Alloy 317L has excellent corrosion resistance to a wide range of chemicals. It resists attack in sulfuric acid, acidic chlorine and phosphoric acid. It is used in handling hot organic and fatty acids often present in food and pharmaceutical processing applications.

The corrosion resistance of 317 and 317L should be the same in any given environment. The one exception is where the alloy will be exposed to temperatures in the chromium carbide precipitation range of 800 – 1500°F (427 – 816°C). Because of its low carbon content, 317L is the preferred material in this service to guard against intergranular corrosion.

In general, austenitic stainless steels are subject to chloride stress corrosion cracking in halide service. Although 317L is somewhat more resistant to stress corrosion cracking than 304/304L stainless steels, because of its higher molybdenum content, it is still susceptible.

The higher chromium, molybdenum and nitrogen content of 317L enhance its ability to resist pitting and crevice corrosion in the presence of chlorides and other halides. The Pitting Resistance Equivalent including Nitrogen number (PREN) is a relative measure of pitting resistance. The following chart offers a comparison Alloy 317L and other austenitic stainless steels.

Machinability

Grade 317 stainless steel is tougher than 304 stainless steel. It is recommended to use chip breakers. Hardenability of this alloy will be reduced if constant feeds and low speeds are used.

Welding

Grade 317 stainless steel can be welded using fusion and resistance methods. Oxyacetylene welding method is not preferred for this alloy. AWS E/ER317 or 317L filler metal can be used to obtain good result.

Hot Working

Grade 317 stainless steel can be hot worked using all common hot working procedures. It is heated at 1149-1260°C (2100-2300°F). It should not be heated below 927°C (1700°F). Post-work annealing can be done to retain the corrosion resistance property.

Cold Working

Stamping, shearing, drawing, and heading can be done successfully. Post-work annealing is performed in order to reduce internal stress.

Annealing

Grade 317 stainless steel is annealed at 1010-1121°C (1850-2050°F) followed by cooling.